kaneka paste pvc

Kaneka’s paste PVC is one of its excellent products manufacturered in Japan and Malaysia.

Used in a variety of fields, Kaneka has a complete line up of grade and blend resins and in order to meet the diverse demands of the market as well as advances in processing technology, Kaneka continues to carry out research for new product types and applications

High K Value Grade (PSH)

Grade	K Value	Paste Viscosity¹⁾ (mPa/s)	Volatile Content (%)	Bulk Density (g/ml)	Particle Size 150μm on	Properties²⁾	Example Applications
PSH-10	75	3000	0.8 or less	Approx. 0.30	10ppm or less	Low viscosity, low water absorbency Greater electrical resistance	Regular, body sealer Toys, electrical components
PSH-31	77	3000	0.8 or less	Approx. 0.30	10ppm or less	Low viscosity, good for foam-forming cells Good sol defoaming properties	PVC steel plate Chemically embossed wallpaper
PSH-24	87	2500	0.8 or less	Approx. 0.30	10ppm or less	High physical properties Good resistance to draw-down	Leathers for automobile use

Mid K Value Grade (PSM)

Grade	K Value	Paste Viscosity¹⁾ (mPa/s)	Volatile Content (%)	Bulk Density (g/ml)	Particle Size 150μm on	Properties²⁾	Example Applications
PSM-30	72	3000*	0.8 or less	Approx. 0.30	10ppm or less	Good sol defoaming properties Good properties for resisting gumming up	Sailcloth, gloves
PSM-31	72	3500	0.8 or less	Approx. 0.30	10ppm or less	Good sol defoaming properties Low viscosity, good foam-forming properties	Cellular leathers, sol
PSM-271R	69	9000	0.8 or less	Approx. 0.30	10ppm or less	Low H.S. viscosity, high thixotropy Good foam-forming properties	Rotary screen method wallpaper

Low K Value Grade (PSL)

Grade	K Value	Paste Viscosity¹⁾ (mPa/s)	Volatile Content (%)	Bulk Density (g/ml)	Particle Size 150μm on	Properties²⁾	Example Applications
PSL-31	66	3000	0.8 or less	Approx. 0.30	10ppm or less	Good foam-forming properties (continuous foam)	Wallpapers Flooring material foam layer
PSL-275	60	3000	0.8 or less	Approx. 0.30	10ppm or less	Low L.S. viscosity, low H.S. viscosity Appropriate for use as high filler and high foam forming	Wallpapers
PSL-290R	64	14000	0.8 or less	Approx. 0.30	10ppm or less	Low H.S. viscosity, high thixotropy Good for foam-forming cells	Rotary screen method wallpaper

Blend Resin Grade (PBM) (Reduced viscosity type)

Grade	K Value	Paste Viscosity¹⁾ (mPa/s)	Volatile Content (%)	Bulk Density (g/ml)	Particle Size 150μm on	Properties²⁾	Example Applications
PBM-6	66	0.6 or less	Approx. 0.45	2 ppm or less	Approx. 36	Good gelatinization properties VAc: 3%	Body sealer, under body coat
PBM-B5F	68	0.4 or less	Approx. 0.55	2 ppm or less	Approx. 40	Reduced viscosity, greater mat effect High physical properties	Flooring, wallpapers
PS-300K	69	0.4 or less	Approx. 0.36	2 ppm or less	Approx. 26	Good rotary screen characteristics	Rotary screen method wallpaper
XPS-300L	–	0.4 or less	Approx. 0.36	2 ppm or less	Approx. 26	Good rotary screen characteristics Greater mat effect	Rotary screen method wallpaper